CHEMICAL ANALYSIS (ALL GRADES) | |
Calcium Carbonate as CaCO3 | 99.0% |
Magnesium as MgO (max.) | 0.1% |
Iron as Fe2 O3 (max.) | 0.01% |
Silica as SiO2 (max.) | 0.10-0.30% |
Aluminium as Al2 O3 (max.) | 0.02% |
PHYSICAL ANALYSIS | |||||||||
PROPERTIES | GRADE | ||||||||
EG-17 | EG-20 | EG-25 | EG-30 | EG-40 | EG-50 | EG-60 | EG-70 | EG-80 | |
Whiteness (±0.50) By Konica Minolta | 97.5% | 97.5% | 97.5% | 97.5% | 98% | 98% | 98.5% | 98.5% | 98.5% |
Moisture (max.) | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% |
Oil Absorption(ml/100gm)±0.50 | 14.5 | 17.0 | 17.0 | 18.5 | 19.5 | 20.5 | 21.5 | 22.5 | 23.5 |
Ph | 9 | 9 | 9 | 9 | 9 | 9 | 9 | 9 | 9 |
D50 (Average particle size (By Malvern 3000E basic ) (µm) |
6-7 | 4-5 | 3.5-4.5 | 3-4 | 2.5-3.0 | 2.0-2.2 | 1.5-1.7 | 1.2-1.3 | 0.9-1.0 |
D97 (Top cut) (By Malvern 3000E basic) (µm) | 34-36 | 23-25 | 19-21 | 16-18 | 11-13 | 8-9 | 5-6 | 4-5 | 3-4 |
CHEMICAL ANALYSIS (ALL GRADES) | |
Calcium Carbonate as CaCO3 | 99.0% |
Magnesium as MgO (max.) | 0.1% |
Iron as Fe 2 O3 (max.) | 0.01% |
Silica as SiO2 (max.) | 0.10-0.30% |
Aluminium as Al2 O3 (max.) | 0.02% |
PHYSICAL ANALYSIS | |||||||
PROPERTIES | GRADE | ||||||
EG-20T | EG-30T | EG-40T | EG-50T | EG-60T | EG-70T | ||
Whiteness (±0.50) By Konica Minolta | 97.5% | 97.5% | 98% | 98% | 98.5% | 98.5% | |
Moisture (max.) | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% | 0.2% | |
Oil Absorption(ml/100gm)±0.50 | 17.0 | 18.0 | 19.5 | 20.5 | 21.5 | 22.5 | |
Ph | 9 | 9 | 9 | 9 | 9 | 9 | |
D50 (Average particle size) (By Malvern 3000E basic ) (µm) | 4-5 | 3-4 | 2.5-3.0 | 2.0-2.2 | 1.5-1.7 | 1.2-1.3 | |
D97 (Top cut) (By Malvern 3000E basic) (µm) | 23-25 | 16-18 | 11-13 | 8-9 | 5-6 | 4-5 | |
Coating% | 1.0-1.2 | 1.0-1.2 | 1.0-1.2 | 1.0-1.2 | 1.0-1.2 | 1.0-1.2 |